Technical terms related to plastics (K line)

In this article, I'm going to introduce some technical terms related to plastik.
You may have heard some of these terms before, but we hope to review them.

rotational casting

Powder or paste plastic material is poured into a hollow metal mold and the mold is heated and rotated to form a plastic product.

In this molding process, the plastic material is melted by heat and adheres to the inside of the mold due to centrifugal force, forming a hollow plastic product along the mold.

This molding method is mainly suitable for manufacturing large tanks and the like.

plasticity

When a force is applied to an object to deform it, the deformation does not return to its original state when a certain amount of force is applied.

Thermoplastic resins, such as plastics, show remarkable plasticity in response to heat.

Due to this property, a plastic product that has been deformed by heat can retain its molded shape, but most commodity plastics are deformed by the application of a certain amount of force or heat.

glass transition point

This is the temperature at which the molecules in the amorphous part of a crystalline plastic begin to move when the temperature is raised, independent of intermolecular forces.

Below this temperature, the plastic is in a glassy state, and above that it is in a rubbery state.

If the temperature is raised further, it reaches the melting point, where the plastic melts.

Casting

In this molding method, liquid monomers with hardening agents are poured into molds made of glass plates and other materials and polymerized before they are removed.

This is a molding method for making plate plastic products, and is mainly used for manufacturing acrylic resin plates.

coincide

It refers to producing a polymer from two or more types of monomers.

A copolymer made from two types of monomers is called a "copolymer," and in the case of three types of monomers Turpolymer.

Copolymers are "random copolymerization," "alternating copolymerization," and "block copolymerization" depending on the arrangement of monomers. Graft copolymerization is classified as "graft copolymerization".

high-density polyethylene

Polyethylene polymerized with a catalyst such as a metal oxide at ambient pressure or slight pressure. It has excellent impact resistance, chemical resistance and weather resistance.

It is a plastic with excellent impact and chemical resistance and weather resistance, and was formerly known as JIS K6748:1995. It is defined as "polyethylene with a density of 0.942 or higher" in the US.